产品与市场
Autolad1
特点
● 无铅兼容FR-4.0板材
● 低的Z轴热膨胀系数
● 优良的耐CAF及TCT性能
● 较低的吸水率
应用领域
● 汽车电子专用材料，适用于车内电路接线盒、发动机和车身的电子控制单元- 产品性能
- 产品证书
- 资料下载
| Items | Method | Condition | Unit | Typical Value |
|---|---|---|---|---|
| Tg | 2.4.24.4 | DMA | ℃ | 165 |
| 2.4.25D |
DSC |
156 | ||
| Td | 2.4.24.6 | 5% wt. loss | ℃ | 353 |
|
T288 |
2.4.24.1 | TMA | min | 25 |
| T260 |
2.4.24.1 |
TMA |
min |
>60 |
|
Thermal Stress |
2.4.13.1 |
288℃, solder dip |
- |
>100 |
| CTE (Z-axis) | 2.4.24 | Before Tg | ppm/℃ | 37 |
| After Tg | ppm/℃ | 210 | ||
| 50-260℃ | % | 2.8 | ||
| Permittivity (10GHz) | 2.5.5.5 | C-24/23/50 | - |
3.89 |
|
Loss Tangent (10GHz) |
2.5.5.5 |
C-24/23/50 |
- | 0.0145 |
| Volume Resistivity | 2.5.17.1 | C-96/35/90 | MΩ/cm | 2.7×108 |
|
Surface Resistivity |
2.5.17.1 |
C-96/35/90 | MΩ | 4.2×107 |
| Arc Resistance | 2.5.1 | D-48/50+D-0.5/23 | s | 150 |
| Dielectric Breakdown | 2.5.6 | D-48/50+D-0.5/23 | kV | >45 |
| Peel Strength (1Oz) | 2.4.8 | 288℃/10s | N/mm[lb/in] | 1.25[7.15] |
| Flexural Strength(LW/CW) | 2.4.4 | A | MPa | 538/425 |
| Water Absorption | 2.6.2.1 | E-1/105+D-24/23 | % | 0.09 |
|
Flammability |
UL94 |
C-48/23/50 |
Rating |
V-0 |
| CTI | IEC60112 | A | Rating | PLC3 |
Remarks:
1. All the typical value is based on the 1.6mm specimen. Test method is according to IPC-TM-650.2. All the typical values listed above are for your reference only and not intended fors pecification. Please contact Shengyi Technology Co., Ltd. for detailed information. All rights from this data sheet are reserved by Shengyi Technology Co., Ltd.
Explanation: C=Humidity conditioning, D=Immersion conditioning in distilled water, E=Temperature conditioning
The first digit following the letter indicates the duration of preconditioning in hours, the second digit the preconditioning temperature in ℃ and the third digit the relative humidity.